氫氧化鉀在常溫下腐蝕不嚴重，但在高溫和應力作用下會嚴重腐蝕很多金屬。鋼在常溫下可在稀氫氧化鈉溶液中使用，但會隨著溫度或濃度的升高而迅速腐蝕。那么檢查工業氫氧化鉀的注意標準和問題理解有哪些呢？

The corrosion of potassium hydroxide is not serious under normal temperature, but it will seriously corrode many metals under high temperature and stress. Steel can be used in dilute sodium hydroxide solution at room temperature, but it will corrode rapidly with the increase of temperature or concentration. What are the standards for attention and understanding of problems in checking industrial potassium hydroxide?

工業氫氧化鉀檢驗注意標準

Standard for inspection of industrial potassium hydroxide

以氫氧化鉀礦石和硫磺為原料生產的工業氫氧化鉀產品的質量檢驗分為出廠檢驗和型式檢驗兩種。一般情況下，型式試驗應每月進行一次。

The quality inspection of industrial potassium hydroxide products produced from potassium hydroxide ore and sulfur can be divided into factory inspection and type inspection. In general, the type test shall be conducted once a month.

分批檢驗，將每個儲罐視為一個批次產品，按規定取樣。每批抽取的樣品總量不得少于500ml。混合后，將樣品裝入帶有研磨塞的干凈、干燥的玻璃小瓶中。瓶子上應標明生產廠家名稱、產品名稱、批號、類別、等級、取樣日期和取樣人員姓名。

For batch inspection, each storage tank shall be regarded as a batch of products and sampled as required. The total amount of samples taken from each batch shall not be less than 500ml. After mixing, the sample is placed in a clean, dry glass vial with a grinding plug. The bottle shall be marked with the name of the manufacturer, product name, batch number, category, grade, sampling date and the name of the sampling personnel.

工業氫氧化鉀檢驗中有一項不符合要求的，一般情況下可重復抽取雙份樣品進行檢驗。產品不合格的，產品資金不得用于銷售，即生產企業按照標準進行生產加工，保障客戶權益。

If one item of industrial potassium hydroxide fails to meet the requirements, double samples can be taken repeatedly for inspection under normal circumstances. If the product is unqualified, the product funds shall not be used for sales, that is, the production enterprise shall carry out production and processing in accordance with national standards to protect the rights and interests of customers.

了解檢查工業氫氧化鉀時的問題

Understand the problems when checking industrial potassium hydroxide

氫氧化鉀在常溫下無腐蝕性，但在高溫和應力作用下會對許多金屬造成嚴重腐蝕。不同溫度下不同濃度氫氧化鈉溶液的設備和管道材料不同，氫氧化鈉溶液濃度為0～30%。如果溫度低于50℃，則采用I類材料制造的設備和管道一般具有耐腐蝕能力；而50～100℃的0%～30%氫氧化鈉溶液對采用耐腐蝕Ⅱ類材料制成的設備和管道具有更好的性能。

Potassium hydroxide is non corrosive at room temperature, but it will cause serious corrosion to many metals under high temperature and stress. The equipment and pipeline materials with different concentrations of sodium hydroxide solution at different temperatures are different. The concentration of sodium hydroxide solution is 0 ~ 30%. If the temperature is lower than 50 ℃, the equipment and pipelines made of class I materials generally have corrosion resistance; However, 0% ~ 30% sodium hydroxide solution at 50 ~ 100 ℃ has better performance for equipment and pipelines made of corrosion-resistant class II materials.

對氫氧化鈉有良好的耐腐蝕性，其次是鎳。銀和鎳可以承受所有濃度和溫度下的氫氧化鈉，直熔化(480°C)。適用于高溫、高濃度堿，鎳及其合金（如Inconel、Monel等）是選擇。不銹鋼能耐40%～50%以下的NaOH溶液80～100℃，但不能耐高濃度和高溫堿液。碳鋼在低溫稀NaOH溶液中具有良好的耐蝕性，并能在表面形成固體氧化物保護膜。由于低廉，往往是很多用戶的選擇。

It has good corrosion resistance to sodium hydroxide, followed by nickel. Silver and nickel can withstand sodium hydroxide at all concentrations and temperatures until melting (480 ° C). It is suitable for high temperature and high concentration alkali. Nickel and its alloys (such as Inconel, Monel, etc.) are the choice. Stainless steel can withstand 80 ~ 100 ℃ of NaOH solution below 40% ~ 50%, but can not withstand high concentration and high temperature alkaline solution. Carbon steel has good corrosion resistance in low temperature dilute NaOH solution, and can form solid oxide protective film on the surface. Because of its low price, it is often the choice of many users.

氫氧化鉀不定型的原因有三：一是氫氧化鉀中常見的金屬離子雜質的存在會影響產品的穩定性。因此，在生產過程中，通常會加入大量的穩定劑來抑制雜質的催化作用。其次，氫氧化鉀在低溫下比較穩定。工業氫氧化鉀加熱到153℃以上會發生爆炸。第三，介質的pH值對工業氫氧化鉀的穩定性影響很大。在酸性介質中，性能更穩定，氧化反應更慢。在堿性介質中，易分解。同時，在這種條件下，過量的工業氫氧化鉀可以通過加熱完全破壞。

There are three reasons for the amorphous potassium hydroxide: first, the presence of common metal ion impurities in potassium hydroxide will affect the stability of the product. Therefore, in the production process, a large number of stabilizers are usually added to inhibit the catalysis of impurities. Secondly, potassium hydroxide is relatively stable at low temperature. Industrial potassium hydroxide will explode when heated above 153 ℃. Third, the pH value of the medium has a great influence on the stability of industrial potassium hydroxide. In acid medium, the performance is more stable and the oxidation reaction is slower. It is easy to decompose in alkaline medium. At the same time, under this condition, excessive industrial potassium hydroxide can be completely destroyed by heating.

以上就是今天為大家分享的關于問題的相關內容，希望對大家能有所幫助，想要了解更多內容可以電話聯系我們或者關注我們的網站http://m.wenping365.com。

The above is the relevant content about the problem shared for you today. I hope it can help you. If you want to know more, you can contact us by phone or follow our website http://m.wenping365.com 。